T1 - Extrusion-based additive manufacturing of Mg-Zn alloy scaffolds
AU - Dong, J.
AU - Tümer, N.
AU - Leeflang, M. A.
AU - Taheri, P.
AU - Fratila-Apachitei, L. E.
AU - Mol, J. M.C.
AU - Zadpoor, A. A.
AU - Zhou, J.
PY - 2022
Y1 - 2022
N2 - Porous biodegradable Mg and its alloys are considered to have a great potential to serve as ideal bone substitutes. The recent progress in additive manufacturing (AM) has prompted its application to fabricate Mg scaffolds with geometrically ordered porous structures. Extrusion-based AM, followed by debinding and sintering, has been recently demonstrated as a powerful approach to fabricating such Mg scaffolds, which can avoid some crucial problems encountered when applying powder bed fusion AM techniques. However, such pure Mg scaffolds exhibit a too high rate of in vitro biodegradation. In the present research, alloying through a pre-alloyed Mg-Zn powder was ultilized to enhance the corrosion resistance and mechanical properties of AM geometrically ordered Mg-Zn scaffolds simultaneously. The in vitro biodegradation behavior, mechanical properties, and electrochemical response of the fabricated Mg-Zn scaffolds were evaluated. Moreover, the response of preosteoblasts to these scaffolds was systematically evaluated and compared with their response to pure Mg scaffolds. The Mg-Zn scaffolds with a porosity of 50.3% and strut density of 93.1% were composed of the Mg matrix and MgZn2 second phase particles. The in vitro biodegradation rate of the Mg-Zn scaffolds decreased by 81% at day 1, as compared to pure Mg scaffolds. Over 28 days of static immersion in modified simulated body fluid, the corrosion rate of the Mg-Zn scaffolds decreased from 2.3 ± 0.9 mm/y to 0.7 ± 0.1 mm/y. The yield strength and Young's modulus of the Mg-Zn scaffolds were about 3 times as high as those of pure Mg scaffolds and remained within the range of those of trabecular bone throughout the biodegradation tests. Indirect culture of MC3T3-E1 preosteoblasts in Mg-Zn extracts indicated favorable cytocompatibility. In direct cell culture, some cells could spread and form filopodia on the surface of the Mg-Zn scaffolds. Overall, this study demonstrates the great potential of the extrusion-based AM Mg-Zn scaffolds to be further developed as biodegradable bone-substituting biomaterials.
AB - Porous biodegradable Mg and its alloys are considered to have a great potential to serve as ideal bone substitutes. The recent progress in additive manufacturing (AM) has prompted its application to fabricate Mg scaffolds with geometrically ordered porous structures. Extrusion-based AM, followed by debinding and sintering, has been recently demonstrated as a powerful approach to fabricating such Mg scaffolds, which can avoid some crucial problems encountered when applying powder bed fusion AM techniques. However, such pure Mg scaffolds exhibit a too high rate of in vitro biodegradation. In the present research, alloying through a pre-alloyed Mg-Zn powder was ultilized to enhance the corrosion resistance and mechanical properties of AM geometrically ordered Mg-Zn scaffolds simultaneously. The in vitro biodegradation behavior, mechanical properties, and electrochemical response of the fabricated Mg-Zn scaffolds were evaluated. Moreover, the response of preosteoblasts to these scaffolds was systematically evaluated and compared with their response to pure Mg scaffolds. The Mg-Zn scaffolds with a porosity of 50.3% and strut density of 93.1% were composed of the Mg matrix and MgZn2 second phase particles. The in vitro biodegradation rate of the Mg-Zn scaffolds decreased by 81% at day 1, as compared to pure Mg scaffolds. Over 28 days of static immersion in modified simulated body fluid, the corrosion rate of the Mg-Zn scaffolds decreased from 2.3 ± 0.9 mm/y to 0.7 ± 0.1 mm/y. The yield strength and Young's modulus of the Mg-Zn scaffolds were about 3 times as high as those of pure Mg scaffolds and remained within the range of those of trabecular bone throughout the biodegradation tests. Indirect culture of MC3T3-E1 preosteoblasts in Mg-Zn extracts indicated favorable cytocompatibility. In direct cell culture, some cells could spread and form filopodia on the surface of the Mg-Zn scaffolds. Overall, this study demonstrates the great potential of the extrusion-based AM Mg-Zn scaffolds to be further developed as biodegradable bone-substituting biomaterials.
KW - Additive manufacturing
KW - Biodegradation
KW - Magnesium-zinc alloy
KW - Material extrusion
KW - Porous scaffold
UR - http://www.scopus.com/inward/record.url?scp=85121125262&partnerID=8YFLogxK
U2 - 10.1016/j.jma.2021.11.018
DO - 10.1016/j.jma.2021.11.018
M3 - Article
AN - SCOPUS:85121125262
SN - 2213-9567
VL - 10
SP - 2491
EP - 2509
JO - Journal of Magnesium and Alloys
JF - Journal of Magnesium and Alloys
IS - 9
ER -