Oxygen-alloyed poly-Si passivating contacts for high-thermal budget c-Si heterojunction solar cells

Research output: Contribution to journalArticleScientificpeer-review

9 Citations (Scopus)
112 Downloads (Pure)

Abstract

Crystalline silicon solar cells with passivating contacts based on doped poly-Si exhibit high optical parasitic losses. Aiming at minimizing these losses, we developed the oxygen-alloyed poly-Si (poly-SiOx) as suitable material for passivating contacts. From passivation point of view, poly-SiOx layers show excellent passivation quality and carrier selectivity for both n-type (iVOC,flat = 740 mV, contact resistance ρc = 0.7 mΩ/cm2, iVOC,textured = 723 mV) and p-type (iVOC,flat = 709 mV, ρc = 0.5 mΩ/cm2). Optically, due to the incorporation of oxygen, the absorption coefficient of poly-SiOx becomes much lower than that of doped poly-Si at long wavelength. Both n-type and p-type poly-SiOx layers are concurrently deployed in front/back-contacted (FBC) solar cells with a front indium tin oxide (ITO) layer to facilitate the lateral transport of carriers and minimize cell's reflection. A high cell FF of 83.5% obtained in double-side flat FBC solar cell indicates an efficient carrier collection by these passivating contacts. An active-area cell efficiency of 21.0% featuring JSC,EQE = 39.7 mA/cm2 is obtained in front-side textured poly-SiOx FBC cell, with the potential of further improvement in both VOC and FF. The optical advantage of poly-SiOx over poly-Si as passivating contact is also observed with a 19.7% interdigitated back-contacted (IBC) solar cell endowed with poly-SiOx emitter and back surface field. Compared to the reference 23.0% IBC solar cell with poly-Si passivating contacts, the one based on poly-SiOx passivating contacts shows higher IQE at wavelengths above 1100 nm. This indicates that for both FBC and IBC cells, poly-SiOx passivating contacts hold potential in enhancing the cell JSC by maximizing the cell spectral response.
Original languageEnglish
Pages (from-to)141-151
Number of pages11
JournalProgress in Photovoltaics: research and applications
Volume30
Issue number2
DOIs
Publication statusPublished - 2022

Fingerprint

Dive into the research topics of 'Oxygen-alloyed poly-Si passivating contacts for high-thermal budget c-Si heterojunction solar cells'. Together they form a unique fingerprint.

Cite this