Core–shell structured gold nanoparticles as carrier for ¹⁶⁶Dy/¹⁶⁶Ho in vivo generator

Background: Radionuclide therapy (RNT) has become a very important treatment modality for cancer nowadays. Comparing with other cancer treatment options, sufficient efficacy could be achieved in RNT with lower toxicity. β⁻ emitters are frequently used in RNT due to the long tissue penetration depth of the β⁻ particles. The dysprosium-166/holmium-166 (¹⁶⁶Dy/¹⁶⁶Ho) in vivo generator shows great potential for treating large malignancies due to the long half-life time of the mother nuclide ¹⁶⁶Dy and the emission of high energy β⁻ from the daughter nuclide ¹⁶⁶Ho. However, the internal conversion occurring after β⁻ decay from ¹⁶⁶Dy to ¹⁶⁶Ho could cause the release of about 72% of ¹⁶⁶Ho when ¹⁶⁶Dy is bound to conventional chelators. The aim of this study is to develop a nanoparticle based carrier for ¹⁶⁶Dy/¹⁶⁶Ho in vivo generator such that the loss of the daughter nuclide ¹⁶⁶Ho induced by internal conversion is prevented. To achieve this goal, we radiolabelled platinum-gold bimetallic nanoparticles (PtAuNPs) and core–shell structured gold nanoparticles (AuNPs) with ¹⁶⁶Dy and studied the retention of both ¹⁶⁶Dy and ¹⁶⁶Ho under various conditions. Results: The ¹⁶⁶Dy was co-reduced with gold and platinum precursor to form the ¹⁶⁶DyAu@AuNPs and ¹⁶⁶DyPtAuNPs. The ¹⁶⁶Dy radiolabelling efficiency was determined to be 60% and 70% for the two types of nanoparticles respectively. The retention of ¹⁶⁶Dy and ¹⁶⁶Ho were tested in MiliQ water or 2.5 mM DTPA for a period of 72 h. In both cases, more than 90% of both ¹⁶⁶Dy and ¹⁶⁶Ho was retained. The results show that the incorporation of ¹⁶⁶Dy in AuNPs can prevent the escape of ¹⁶⁶Ho released due to internal conversion. Conclusion: We developed a chelator-free radiolabelling method for ¹⁶⁶Dy with good radiolabelling efficiency and very high stability and retention of the daughter nuclide ¹⁶⁶Ho. The results from this study indicate that to avoid the loss of the daughter radionuclides by internal conversion, carriers composed of electron-rich materials should be used.