Thermal quenching of Eu2+ emission in Ca- and Sr-Ga2S4 in relation with VRBE schemes

A.P. Dobrowolska, Benjamin Dierre, C.M. Fang, Bert Hintzen, Pieter Dorenbos

Research output: Contribution to journalArticleScientificpeer-review

9 Citations (Scopus)
39 Downloads (Pure)

Abstract

Structural and optical properties of MGa2S4 (M = Mg, Zn, Ca, Sr, Ba) compounds have been compared, and the vacuum referred binding energy (VRBE) schemes were constructed for the lanthanide ions in the iso-structural compounds CaGa2S4 and SrGa2S4 employing literature data. The VRBE of an electron in the 5d excited state of Eu2+ was found at 0.75 and 0.97 eV below the bottom of the conduction band (CB) in CaGa2S4:Eu and SrGa2S4:Eu, respectively. Such differences explains the unexpected higher thermal quenching temperature reported for Eu2+-doped SrGa2S4 (T50% = ∼475 K) compared to Eu2+-doped CaGa2S4 (T50% = 400 K) The significantly lower VRBE at the CB-bottom in CaGa2S4 versus SrGa2S4 may be explained by the shorter Ga-S bond lengths in SrGa2S4.
Original languageEnglish
Pages (from-to)256-261
JournalJournal of Luminescence
Volume184
DOIs
Publication statusPublished - 27 Dec 2016

Bibliographical note

Accepted Author Manuscript

Keywords

  • SrGa2S4
  • CaGa2S4
  • Thiogallate
  • VRBE
  • Thermal quenching