Investigation of Structure, Ionic Conductivity, and Electrochemical Stability of Halogen Substitution in Solid-State Ion Conductor Li₃YBr_xCl_{6- x}

Li₃YX₆(X = Cl, Br) materials are Li-ion conductors that can be used as solid electrolytes in all solid-state batteries. Solid electrolytes ideally have high ionic conductivity and (electro)chemical compatibility with the electrodes. It was proven that introducing Br to Li₃YCl₆increases ionic conductivity but, according to thermodynamic calculations, should also reduce oxidative stability. In this paper, the trade-off between ionic conductivity and electrochemical stability in Li₃YBr_xCl_6-xhalogen-substituted compounds is investigated. The compositions of Li₃YBr_1.5Cl_4.5and Li₃YBr_4.5Cl_1.5are reported for the first time, along with a consistent analysis of the whole Li₃YBr_xCl_6-x(x = 0-6) tie-line. The results show that, while Br-rich materials are more conductive (5.36 × 10^-3S/cm at 30 °C for x = 4.5), the oxidative stability is lower (∼ 3 V compared to ∼ 3.5 V). Small Br content (x = 1.5) does not affect oxidative stability but substantially increases ionic conductivity compared to pristine Li₃YCl₆(2.1 compared to 0.049 × 10^-3S/cm at 30 °C). This work highlights that optimization of substitutions in the anion framework provide prolific and rational avenues for tailoring the properties of solid electrolytes.